| Descripstion | GRADE | Size | SCH | PRICE PER
TON IN USD |
|---|---|---|---|---|
| Carbon steel SMLS Pipe | api 5l x56 psl1 pipe
api 5l x56 psl2 pipe | 1/2” To 24” | 10, 20, 30, STD, 40, 60, XS, 80, 100, 120, 140, 160, XXS | 1200 TO 1400 |
| Carbon steel SMLS Pipe | api 5l x56 psl1 pipe
api 5l x56 psl2 pipe | 1/2” To 24” | 10, 20, 30, STD, 40, 60, XS, 80, 100, 120, 140, 160, XXS | 1400 TO 2000 |
| Carbon steel ERW, LSAW, SAW, EFW Pipe | api 5l x56 psl1 pipe
api 5l x56 psl2 pipe | 16” To 84” | 10, 20, 30, STD, 40, 60, XS, 80, 100, 120, 140, 160, XXS | 800 TO 1000 |
| Carbon steel ERW, LSAW, SAW, EFW Pipe | api 5l x56 psl1 pipe
api 5l x56 psl2 pipe | 16” To 84” | 10, 20, 30, STD, 40, 60, XS, 80, 100, 120, 140, 160, XXS | 1000 TO 1300 |
| Note:- | |
|---|
| Trade name | API 5L X56 PSL1 Pipe |
| Other Specification | |
| Available | API 5L – A,B, X – 42, 46, 52, 56, |
| 60, 65, 70, 80 | |
| Special Tube | Saw Pipes & Steam Pipes |
| Precision Tubes | |
| Fabricated Pipe (with radiography) | |
| In Form of | Round |
| Hydraulic Tube & | |
| Horn Tube. | |
| In Length of | Standard |
| Double & | |
| In Cut length also. | |
| Value Added Service | Draw & Expansion as per required Size & Length |
| Heat Treatment | |
| Bending | |
| Galvanizing | |
| Annealed | |
| Sand Blasting | |
| Machining Etc. | |
| Test Certificate | Manufacturer Test Certificate |
| IBR Test Certificate (Form III-D) | |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection with Excise Gate Pass to avail | |
| Modvat benefit. | |
| API 5L X56 | (PSL1) | (PSL2) |
|---|
| Minimum Yield Strength: | 56,600 psi | 56,600 psi |
| Maximum Yield Strength: | None | 79,000 psi |
| Minimum Tensile Strength: | 71,100 psi | 71,100 psi |
| Maximum Tensile Strength: | None | 110,200 psi |
| Notes: This is a standard line pipe grade specified in API (American Petroleum Institute) specification 5L. | | |
Line pipe – types of steel
Chemical Analysis(%) For Part Standard
| Standard | Class | Grade | C | Si | Mn | P | S | V | Nb | Ti |
|---|
| max | max | max | max | max | max | max | max | | | |
| APL 5L | | | | | | | | | | |
| ISO 3181 | PSL1 | L245 or B | 0.26 | - | 1.20 | 0.030 | 0.030 | - | - | - |
| L290 or X42 | 0.26 | - | 1.30 | 0.030 | 0.030 | - | - | - | | |
| L320 or X46 | 0.26 | - | 1.40 | 0.030 | 0.030 | a,b | a,b | b | | |
| L360 or X52 | 0.26 | - | 1.40 | 0.030 | 0.030 | b | b | b | | |
| L390 or X56 | 0.26 | - | 1.40 | 0.030 | 0.030 | b | b | b | | |
| L415 or X60 | 0.26 | - | 1.40 | 0.030 | 0.030 | c | c | c | | |
| L450 or X65 | 0.26 | - | 1.45 | 0.030 | 0.030 | c | c | c | | |
| L485 or X70 | 0.26 | - | 1.65 | 0.030 | 0.030 | c | c | c | | |
Mechanical Properties
| Standard | Specified Outside Diameter | Grade | Charp Imapct Test 0℃ | |
|---|
| Impact of Pipe Body | Impact of Weld | | | |
| API 5L | | | | |
| ISO3183 | D≤762mm | ≤L485 or X70 | 27 | 27 |
| L555 or X80 | 40 | 27 | | |
| 762mm< td="" style=“box-sizing: border-box;”><> | ≤L555 or X80 | 40 | 27 | |
| 1219mm< td="" style=“box-sizing: border-box;”><> | ≤L415 or X60 | 40 | 27 | |
| >L415 or X60 | | | | |
| ≤L555 or X80 | 54 | 27 | | |
| >1422mm | ≤L415 or X60 | 40 | 40 | |
| >L415 or X60 | | | | |
| ≤L555 or X80 | 54 | 40 | | |
| Standard | Class | Grade | Yield Strength
MPa | Yield Strength
MPa | Y.S/T.S | | |
|---|---|---|---|---|---|---|---|
| min | max | min | max | max | | | |
| API 5L
ISO3183 | PSL2 | L245R or BR
L245N or BN
L245Q or BQ
L245M or BM | 245 | 450 | 415 | 655 | 0.93 |
| L290R or X42R
L290N or X42N
L290Q or X42Q
L290M or X42M | 290 | 495 | 415 | 655 | 0.93 | | |
| L320N or X46N
L320Q or X46Q
L320M or X46M | 320 | 525 | 435 | 655 | 0.93 | | |
| L360N or X52N
L360Q or X52Q
L360M or X52M | 360 | 530 | 460 | 760 | 0.93 | | |
| L390N or X56N
L390Q or X56Q
L390M or X56M | 390 | 545 | 490 | 760 | 0.93 | | |
| L415N or X60N
L415Q or X60Q
L415M or X60M | 415 | 565 | 520 | 760 | 0.93 | | |
| L450Q or X65Q
L450M or X65M | 450 | 600 | 535 | 760 | 0.93 | | |
| L485Q or X70Q
L485M or X70M | 485 | 635 | 570 | 760 | 0.93 | | |
| L555Q or X80Q
L555M or X80M | 555 | 705 | 625 | 825 | 0.93 | | |
| L625M or X90M
L625Q or X90Q | 625 | 775 | 695 | 915 | 0.95 | | |
| L690M or X100M
L690Q or X100Q | 690 | 840 | 760 | 990 | 0.97 | | |
Minimum Impact Energy
API 5L X56 PSL1 Pipe – delivery condition and surface
API 5L X56 PSL1 Pipe – straightness
Ends of the API 5L X56 PSL1 Pipe
Marking of API 5L X56 PSL1 Pipe and tube bundles
API 5L X56 PSL1 Pipe – surface protection
| CHEMICAL COMPOSITION | | | | | | | | | | | |
|---|
| Mass fraction, based upon heat and product analysis % maximum | CARBON EQUIVALENT a | | | | | | | | | | |
| % MAXIMUM | | | | | | | | | | | |
| Cb | Si | Mnb | P | S | V | Nb | Ti | Other | CEIIW | CEPcm | |
| SEAMLESS & WELDED PIPES | | | | | | | | | | | |
| L485Q or X70Q | 0.18f | 0.45f | 1.8f | 0.025 | 0.015 | g | g | g | h | 0.43 | 0.25 |
| WELDED PIPE | | | | | | | | | | | |
| L485M OR X70M | 0.12f | 0.45f | 1.7f | 0.025 | 0.015 | g | g | g | h | 0.43f | 0.25 |
| MECHANICAL REQUIREMENTS | | |
|---|
| Y.S | T.S | ELONGATION |
| Mpa(psi) | Mpa(psi) | |
| min | min | min |
| 485(70 300) | 635(92 100) | f |
| IMPACT TEST | |
|---|
| AVG. ABSORBED ENERGY | IND. ABSORBED ENERGY |
| Min.(joules) | Min.(joules) |
| 27 | 20 |